文章采用Foron類分散染料對聚醚砜纖維進行載體染色，通過K/S值和染色牢度對染色效果進行評價。結(jié)果表明：載體Dilatin POE能明顯提高聚醚砜纖維的可染性，隨載體用量增加，纖維強力下降；載體Dilatin POE用量為 0.8 g/L，90 ℃染色45 min時，可達到較好的染色效果，斷裂強力下降 10% 左右；染后聚醚砜纖維具有良好的耐洗和耐摩擦牢度。

In this paper, PES fiber was dyed in carrier dyeing process with Foron dyestuffs. The dyeing performance was evaluated by K/S value and colorfastness. The results showed that Dilatin POE can improve the dyeability of PES fiber consumedly, but the strength of the yarn decreased with the adding of the carrier. Dyeing at 90 ℃ for 45 minutes with 0.8 g/L carrier Dilatin POE has good dyeing effect on PES fiber and the breaking strength of the yarn decreasing about 10%. After dyeing, the colorfastness to washing and rubbing were good.

聚醚砜（PES）樹脂是一種綜合性能優(yōu)異的熱塑性聚合物材料，它具有突出的阻燃性能，極限氧指數(shù)為38，具有自熄性；玻璃化轉(zhuǎn)變溫度為225℃，為無定形材料，連續(xù)使用溫度為180～200℃。最初是作為阻燃性、耐熱性、耐化學藥品性和機械性能等方面都非常優(yōu)異的特種工程塑料開發(fā)出來的，國內(nèi)外極少見有真正在纖維方面進行應用開發(fā)的研究。北京服裝學院采用熔融紡絲法制得了聚醚砜纖維，并應用于航空航天領(lǐng)域的先進復合材料，取得了較好的效果。

將聚醚砜纖維推廣到民用紡織品，就要研究其染色性能。近年來對一些高性能纖維如芳砜綸、芳綸等大多采用載體染色法，以降低染色溫度。考慮到聚醚砜的玻璃化轉(zhuǎn)變溫度也較高，且分子鏈上沒有能與染料分子相結(jié)合的反應性基團，因此采用分散染料對其進行載體染色。

1試驗

1.1材料與藥品

聚醚砜紗線（35tex/24f，自制）；Foron艷紅RD–BR、Foron黃RD–4GRL、Foron藍RD–E（Clariant（科萊恩）公司）；CTC–480導染劑（北京中紡化工有限公司）；環(huán)保型載體DilatinPOE（Clariant公司）；磷酸二氫銨（A.R.）；洗滌劑；無水碳酸鈉（A.R.）；皂粉。

1.2儀器

恒溫水浴鍋（余姚市東方電工儀器廠）、ORINTEX電子測色配色系統(tǒng)（意大利ORINTEX染色技……