基于CBP的高效穩定綠色磷光OLED

徐　瑤,寇志起,程　爽,卜勝利

(上海理工大學 理學院,上海　200093)

?

基于CBP的高效穩定綠色磷光OLED

徐瑤,寇志起,程爽,卜勝利

(上海理工大學 理學院,上海200093)

摘要使用真空蒸鍍法分別制作了以TCTA和CBP做為主體材料的綠色磷光OLED器件,發現采用CBP為主體材料的器件比采用TCTA為主體材料的器件更穩定。之后在采用CBP作為主體材料的器件中分別摻雜了3%,6%,9%的藍色客體磷光材料FIrpic,得出在摻雜濃度為3%時,即器件結構為ITO/HAT-CNTAPC/CBP:8%Ir (ppy)3:3%FIrpic/Tmpypb/Liq/Al時性能最佳。FIrpic摻雜比例為3%時得到最大功率效率和最大電流效率分別為54.3 lm/W和64.8 cd/A,最大亮度為51 940 cd/m2。研究表明Firpic的摻雜,在不改變綠色磷光OLED光譜性能的同時,有助于提高綠色磷光OLED的電光性能。

關鍵詞綠色有機發光二極管;CBP;FIrpic;摻雜

Efficient and Stable Green Phosphoresent OLED Based on CBP

XU Yao,KOU Zhiqi,CHENG Shuang,BU Shengli

(School of Science,University of Shanghai for Science and Technology,Shanghai 200093,China)

AbstractGreen phosphoresent OLEDs have been fabricated by vacuum evaporation with the structure based on TCTA and CBP as the host.We find that it is more stable using CBP as host than TCTA.Then the blue phosphoresent material Firpic is doped into the emitting layer of OLED devices based on CBP with the concentration of 3%,6%,9% respectively.The best performance is found in the structure ITO/HAT-CNTAPC/CBP:8%Ir (ppy)3:3%FIrpic/Tmpypb/Liq/Al.The maximum power efficiency and current efficiency values are 54.3 lm/W and 64.8 cd/A for 3% FIrpic doping respectively,with a maximum luminance of 51 940 cd/m2.Research shows that doping FIrpic into green phosphorescent OLED improves the device’s electro-optic performance without affecting the spectrum of the device.

Keywordsgreen OLED;CBP;FIrpic;doping

自Pope[1]教授在1963年發現了有機電致發光現象后,學術界逐漸開始對OLED器件的研究并取得了快速進展。1987年,美國柯達公司的Tang等人[2]制成了雙層OLED器件,使器件中空穴電子的注入平衡得到了調節,達到提高器件性能的效果。1998年,Forrest等人[3]將磷光材料應用于OLED器件,由于熒光材料只有單線態激子參與發光,而磷光材料的單線態和三線態激子可共同參與發光,為OLED器件實現100%的內量子效率提供了可能。OLED器件相比傳統的發光器件有著輕薄、視角大、抗震、低溫特性好、響應時間快和顯色好等優點,又因其能在不同材質的基板上制造,所以能做成可彎曲的柔性顯示,從而更好的適應人們日趨增長的高品質顯示要求。

OLED器件的發光性能及穩定性還有待于進一步提高,近年來,研究者們通過對發光層的摻雜和結構的改變來改善傳統OLED器件的性能,并已取得了豐碩的成果[4-6]。……