Stable Zirconium Carbide Fibers Fabricated by Centrifugal Spinning Technique

CHEN Bowen, WANG Jingxiao, JIANG Youlin, ZHOU Haijun, LIAO Chunjing, ZHANG Xiangyu, KAN Yanmei, NI Dewei

Stable Zirconium Carbide Fibers Fabricated by Centrifugal Spinning Technique

CHEN Bowen1,2,3, WANG Jingxiao1,2, JIANG Youlin1,2,3, ZHOU Haijun1,2, LIAO Chunjing1,2, ZHANG Xiangyu1,2, KAN Yanmei1,2, NI Dewei1,2

(1. State Key Laboratory of High Performance Ceramics and Super?ne Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China; 2. Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China; 3. University of Chinese Academy of Sciences, Beijing 100049, China)

In this work, an efficient approach was presented to produce stable zirconium carbide (ZrC) fibers by centrifugal spinning technique. Zirconium acetate and sucrose were used as the zirconium source and carbon source respectively. And polyvinyl pyrrolidone (PVP) was used as the spinning aid. After pyrolysis and carbothermal reduction at 1600 ℃, the as-spun green fibers can be converted to homogeneous ZrC fibers composed of uniform nano-sized ZrC crystals. Moreover, it is revealed that the as-fabricated ZrC fibers can sustain superior microstructure stability at an ultra-high temperature up to 2000 ℃, benefiting from a limited amount of residual carbon. The reaction mechanisms and the resulted ZrC fibers were also investigated.

zirconium carbide fiber; centrifugal spinning; ultra-high temperature stability

As a member of the ultra-high temperature ceramics (UHTCs) family, zirconium carbide (ZrC) has an extremely high melting point (3540 ℃), good mechanical properties, and excellent ablation resistance.[1-2], leading to potential applications in the extremely harsh environment associated with hypersonic flight, atmospheric re-entry, and rocket propulsion,.[3-5]. However, the inherent brittleness and poor thermal shock resistance of bulk ceramics have limited its practical application to some extent.

The fiber reinforced UHTCs matrix composites have excellent mechanical properties, ablation resistance at ultra-high temperatures, and overcome the inherent brittleness and poor thermal shock resistance of bulk UHTCs. The UHTCs fibers, applied as the reinforcement fibers, have become the focus of scientific research in the past few decades[6]. To date, ZrC fibers, act as reinforcement, have been developed through a variety of methods, which are normally achieved based on colloid processing and spinning technique, followed by carbothermal reaction at high temperatures. Using the mixtures of cellulose acetate and zirconium-butoxide as precursor, Kurokawa,[7]prepared ZrC fibers with short length (<1 cm) and large diameter (~100 μm) by spinning the precursor gel with a syringe. Electrospinning has attracted a lot of attention in fibers fabrication due to its simplicity and ability to fabricate fibers with diameters down to hundreds of nanometers, which is used in the production of ZrC fibersas well[8]. Nam,[9]produced long continuous ZrC nanofibers by electrospinning and found that the optimized ratio of C/Zr was 5.5 as considering the formation of single phase ZrC with a continuous long fibrous structure. Compared with electrospinning, centrifugal spinning is a highly efficient, low-cost, and versatile method for fibers fabrication. The process uses centrifugalforces coupled with the viscoelastic properties and the mass transfer characteristics of spinning solutions to promote the controlled thinning of a polymer solution filament into fibers. Centrifugal spinning has produced various polymer fibers with good morphologies and high throughput. Recently, Firbas,[10]also developed ZrC fibers by centrifugal spinning, using zirconium--propoxide (zirconia source), furfuryl alcohol (carbon source) and polyvinylpyrrolidone (spinning aids) as starting materials. ZrC fiber can be used as reinforcement in metal matrix composites for nuclear applications, and the extreme service environment askes ZrC fiber must have an excellent high temperature microstructural stability[11]. However, most previous work paid attention to the fabrication process, and the detailed microstructure of the ZrC fibers after high temperature treatment was not presented. Therefore, investigation of high temperature microstructure stability of the fabricated ZrC fibers is critical. In this work, zirconium carbide fibers were fabricated by a centrifugal spinning technique based on an aqueous solution-derived precursor, and the conversion mechanisms from as-spun green fibers to ZrC fibers were investigated in detail. Moreover, the microstructure stability of the synthesized ZrC fibers was investigated at an ultra-high temperature up to 2000 ℃.

1 Experimental procedure

1.1 Materials and processing

Zirconium acetate (ZrO(CH3COO)2, purity 99%), sucrose (C12H22O11, AR grade) and polyvinyl pyrrolidone (PVP,W=1300000) were used as raw materials. The molar ratio between ZrO(CH3COO)2and C12H22O11was set in a range of 4 : 1 to 4 : 1.5 according to the carbothermal reduction reaction between ZrO2and C. The addition of PVP was fixed at ~2wt% of zirconium acetate. To form a uniform precursor, the starting materials were mixed with deionized water under continuous stirring for 24 h. The precursor was injected into the centrifugal spinning (TEADFS-900; Nova Tech Co., Ltd, Beijing, China) spinneret with a 0.5 mm needle. A collector distance of 20 cm was used and the rotational frequency was fixed at 8000 r/min. The environmental temperature was set at 45 ℃ for the spinning.

The obtained fibers were dried at 85 ℃ and then pyrolyzed at 600 ℃ for 2 h under flowing argon atmos-phere with a heating rate of 1 ℃·min–1. Subsequently, the fibers were heat-treated at 1400~1600 ℃ for 2 h in argon at a heating rate of 2 ℃·min–1. Further heat-treatment at 2000 ℃ for 2 h in argon was conducted to study the microstructure stability of the fibers at ultra-high temperatures.

1.2 Characterization

Fourier transform infrared (FT-IR) spectra of the precursors were carried out using NICOLET Is 10 spectro-meters (Thermo Fisher Scientific, Massachusetts, USA). Thermogravimetric and differential scanning calorimetric analysis (TG–DSC) were analyzed by Netzsch STA 499 F3 Jupiter? in argon flow in the temperature range of 40–1400 ℃at the heating rate of 10 ℃·min–1. Phase compositions were determined by X-ray diffraction (XRD, Rigaku Corporation, Kyoto, Japan) using Cu-Kα radiation (40 kV, 40 mA, 10 (°)/min from 10° to 85°).

A field emission scanning electron microscope (FESEM, Merlin Compact, Zeiss, Germany) was applied to observe the morphologies and microstructure of the fibers. Besides, a 200 kV transmission electron microscope (TEM, JEOL JEM-2100F, Japan) was also used to characterize the fibers. The oxygen content of the ZrC fiber was measured by a nitrogen/oxygen determinator (TC600, LECO, St. Joseph, MI). The carbon/sulfur analyzer (CS2000, ELTRA, Germany) was used to determine the carbon content of the as-synthesized fibers.

2 Results and discussion

In this work, ZrC fibers were fabricateda tailor- made centrifugal spinning system. Fig. 1 shows the sche-matic of the centrifugal spinning device and preparation process of ZrC fibers. Based on the theory of rotating centrifuge, the centrifugal spinning device has an adjus-table speed motor to provide suitable speed rotation. The distance between the spinneret and collectors can be ad-justed to provide a proper space for solvent evaporation. The temperature of the spinning environment can also be controlled. Rotation is initiated after loading the ZrC precursor into the spinneret. Liquid jets are formed in case the centrifugal force overcome the surface tension, then stretched in the flight of the circular trajectory accompanied by solvent evaporation and deposited on the collectors. After stabilization and carbothermal reduction, ZrC fibers are obtained. This process is much more efficient as compared with other traditional spinning methods.

Fig. 1 Schematic of the centrifugal spinning system and the preparation of ZrC fibers

Zirconium acetate and sucrose are used as starting re-agents, and polyvinyl pyrrolidone (PVP) is used as spin-ning aid to form a proper precursor for ZrC fibers. The structural evolution and principal interactions of the ZrC precursors were investigated by infrared spectroscope. The FT-IR spectra of the precursors with different ratios of ZrO(CH3COO)2:C12H22O11are shown in Fig. 2, which show similar absorption peaks. The respective assignments of the absorption peaks are 3440 ((O–H) +(NH2)), 2940 ((C–H)), 1655 ((C=O)), 1435 ((C=O) +(CH)), 1030 ((C–O–C)), and 650 ((C–CH3) +(Zr–O) + ring distortion) and 400–500 ((Zr–O)) cm–1[12]. With increased C12H22O11content, the peaks at 2940, 1655, 1030, 650 cm–1shift to lower wavenumbers and the intensity of –C–O–C–, –C–CH3and Zr–O increases slightly. It reveals that the excess sucrose gets involved in complexation.(O–H) and(NH2) are corresponding to the broad peak at ~3440 cm–1which are attributed to the stretching vibration of –NH2and –OH groups. The peak at 1655 cm–1assigned to(C=O) is chelated to zirconium, thus drastically reducing the tendency of zirconium to form bulk gels. Furthermore, absorbed water is revealed by the peaks at around 3440 and 1655 cm–1of the precursor, which is also confirmed by the TG-DSC analysis as shown below. The peaks located at 650 and 495 cm–1are attributed to ring distortion +(Zr–O) of the cyclic structure after the zirconium chelation[13]. Almost all absorption peaks of the precursor disappear after pyrolysis at 600 ℃, which indicates that the pyrolysis process finishes and almost no residual organics exists.

Fig. 2 FT-IR spectra of ZrC precursors with different ZrO(CH3COO)2 : C12H22O11 ratios: (a) 4 : 1; (b) 4 : 1.2; (c) 4 : 1.5; and (d) ZrC precursor (with ZrO(CH3COO)2 : C12H22O11= 4 : 1.5) after pyrolysis at 600 ℃

As shown in Fig. 3, simultaneous TG-DSC analysis was performed for the as-spun green fibers (using the ZrC precursor with ZrO(CH3COO)2: C12H22O11=4 : 1.5). The pyrolysis processes of the green fibers can be seg-mented into four steps. The initial weight loss of 5.35% below 150 ℃ is corresponding to the separation of ad-sorbed water and evaporation of free water. A considerable weight loss of around 9.60% occurred at the temperature range of 150–190 ℃, which is due to the eva-poration of constitution water and organic by products. The first two stages lead to an apparent endothermic peak on the DSC curve. The weight loss of around 29.07% at temperatures between 190 and 500 ℃ is corresponding to the decomposition of ZrO(CH3COO)2, C12H22O11and PVP. At temperatures higher than 500 ℃, the TG curve is almost flat, where the weak weight loss can be attributed to the continuous carbonization of sucrose and the transformation of the ZrO2crystalline phase[14-15]. After that, the carbothermal reduction reaction begins at around 1400 ℃. Therefore, 600 ℃ and 1400~1600 ℃ were set as the pyrolysis and carbothermal reduction temperatures, respectively.

Fig. 4 shows the XRD patterns of ZrC fibers prepared from ZrC precursors with different ZrO(CH3COO)2: C12H22O11ratios after heat-treatment at temperature range of 1400–1600 ℃. At 1400 and 1500 ℃, ZrC forms in the fibers but-ZrO2still exists. Cubic ZrC becomes the only phase for all three ZrC fibers at 1600 ℃, where the oxygen content is determined around 1wt%. As shown in the expanded XRD (inset in Fig. 4), the diffraction peaks shift to lower theta value with the decrease of sucrose in the ZrC precursor. According to the Bragg equation, the lattice parameter of the cubic ZrC was calculated to be 0.46631, 0.46706, and 0.46781 nmrespectively. This implies the formation of non-stoichiometric Zr1?xC according to the reaction of (1–)ZrC+C→Zr1–xC. More Zr vacancies/non-stoichiometric Zr1?xC can be formed with the increase of residual free carbon (value), resulting in a smaller lattice parameter. In previous work, Raman spectra of the synthesized fibers are caricatured. The results indicate that two typical peaks centered at ~1330 and ~1590 cm–1are detected in all three samples, corresponding to the D and G peaks of free carbon. The results reveal the presence of the residual free carbon in the fibers. Chemical analysis indicates that the contents of the residual free carbon in the synthesized ZrC fibers are 1.4wt%, 0.8wt%, and 0.5wt%, respectively[16]. Base on the XRD results, the grain sizes of fibers are calculated by the Debye-Scherrer equation. The grain sizes of the ZrC fibers obtained from the precursor with ZrO(CH3COO)2: C12H22O11ratio of 4 : 1, 4 : 1.2 and 4 : 1.5 are 32.54, 30.90, and 24.23 nm respectively. The content of the residual carbon increases with the decrease of the ZrO(CH3COO)2:C12H22O11ratio. And, the existence of the residual carbon impedes the surface diffusion between ZrC grains which prevents the growth of ZrC grains during the heat treatment process.

Fig. 3 TG-DSC curves of the as-spun green fibers prepared from ZrC precursor with ZrO(CH3COO)2 : C12H22O11=4 : 1.5

Fig. 4 XRD patterns of ZrC fibers prepared from ZrC precursors with different ZrO(CH3COO)2:C12H22O11 ratios after heat- treatment at temperature range from 1400 to 1600 ℃ for 2 h

(a) 4 : 1.5 @1400 ℃; (b) 4 : 1.5 @1500 ℃; (c) 4 : 1.5 @1600 ℃; (d) 4 : 1.2 @1600 ℃; (e) 4 : 1 @1600 ℃

SEM and TEM were used to study the microstructure evolution of the ZrC fibers. As shown in Fig. 5(a), the diameter of as-spun green fibers is around 1–3 μm. It shows a uniform distribution and certain bridges among fibers can be observed. This indicates that the synthesized ZrC precursor solution presents very good spin-ability. Although zirconium acetate, sucrose, and PVP are decomposed and a large number of gas molecules run out during the pyrolysis at 600 ℃, there’s no obvious change in the morphology of the fibers (Fig. 5(b)). After heat-treated at 1600 ℃, the morphology of the ZrC fibers is well preserved, where the surface is smooth and the diameter does not change obviously (Fig. 5(c)). TEM image and SAED pattern shown in Fig. 5(d) confirm that the fibers are composed of well crystallized ZrC nanoparticles (inset in Fig. 5(d)).

Fig. 5 SEM images of ZrC fibers prepared from ZrC precursor with ZrO(CH3COO)2 : C12H22O11=4 : 1.5((a) as-spun green fibers; (b) after heat-treatment at 600 ℃ and (c) after heat- treatment at 1600 ℃); and (d) TEM image of ZrC fibers after heat-treatment at 1600 ℃

The insets in (a,b,c) are the corresponding local enlarged images; while the inset in (d) is the selected area electron diffraction (SAED) pattern of ZrC fibers

Subsequently, the microstructure stability of the syn-thesized ZrC fibers at an ultra-high temperature of 2000 ℃ was investigated. Fig. 6 shows SEM images of the ZrC fibers prepared from ZrC precursors with differ-ent ZrO(CH3COO)2: C12H22O11ratios after heat-treated at 2000 ℃ for 2 h under flowing argon atmosphere. The morphologies and high temperature microstructure sta-bility of the ZrC fibers are strongly influenced by the composition of the initial ZrC precursors. For the ZrC fibers prepared from the precursor with higher ZrO(CH3COO)2:C12H22O11ratio (4 : 1), the ZrC grains of the fibers coarsen seriously and the fibrous structures are destroyed after heat-treated at 2000 ℃ (Fig. 6(a-b)). While for the fibers prepared from ZrC precursors with increased sucrose content, the fibrous structures are well preserved with a smooth surface and limited ZrC grains coarsening (Fig. 6(c-f)). As discussed on the XRD pa-tterns (Fig. 4), residual free carbon exists in the ZrC fibers with the increase of sucrose in the initial precursors. Therefore, it is indicated that the existence of residual carbon is beneficial to retain the morphologies and improve the high temperature microstructure stability of the ZrC fibers. As is known, grain growth mainly occurred among particlessurface diffusion. The existence of the limited amount of residual carbon in the ZrC fibers reduces the ZrC particles’ mutual contact, thus preventing the particle coarsening at high temperature and improve the microstructure stability of the fibers up to 2000 ℃. It can be seen from the cross-sections of the fibers (Fig. 6 (d, f)) that the ZrC grain size of the fibers remains about tens of nanometers even after heat-treated at 2000 ℃.

Fig. 6 SEM images of ZrC fibers prepared from ZrC precursors with different ZrO(CH3COO)2 : C12H22O11 ratios after heat-treatment at 2000 ℃ for 2 h

(a, b) 4 : 1; (c, d) 4 : 1.2; (e, f) 4 : 1.5

3 Conclusions

In summary, ZrC fibers with ultra-high temperature microstructure stability were successfully prepared by a combination of solution-based processing and centrifugal spinning technique. Zirconium acetate, sucrose, and polyvinyl pyrrolidone (PVP) are used as the zirconium source, carbon source, and spinning aid respectively. The as-spun green fibers are converted to homogeneous ZrC fibers composed of uniform nano-sized ZrC crystals after pyrolysis and carbothermal reduction reaction at 1600 ℃. The results show that the small amount of residual free carbon in the fibers can react with ZrC and cause the formation of non-stoichiometric Zr1–xC. Furthermore, the existence of residual free carbon can prevent ZrC particle coarsening and lead to excellent high-temperature microstructure stability of the synthesized ZrC fibers up to 2000 ℃. It is believed that the ZrC fiber with high- temperature microstructure stability would be beneficial for the subsequent application of the materials.

[1] FAHRENHOLTZ W G, HILMAS G E, TALMY I G,Refractory diborides of zirconium and hafnium.., 2007, 90(5): 1347–1364.

[2] ZHANG G J, NI D W, ZOU J,Inherent anisotropy in transition metal diborides and microstructure/property tailoring in ultra- high temperature ceramics—a review.., 2018, 38(2): 371–389.

[3] CHARBONNIER F M, MACKIE W A, HARTMAN R L,Robust high current field emitter tips and arrays for vacuum microelectronics devices.., 2001, 19(3): 1064–1072.

[4] COCKERAM B V, MEASURES D P, MUELLER A J. The development and testing of emissivity enhancement coatings for themophotovoltaic (TPV) radiator applications., 1999, 355(1): 17–25.

[5] SHEATS J R, MACKIE W A, ANZ S,Polymer electroluminescent devices with zirconium carbide cathodes., 1997, 3148: 219–227.

[6] LI F, KANG Z, HUANG X,Fabrication of zirconium carbide nanofibers by electrospinning., 2014, 40(7): 10137–10141.

[7] KUROKAWA Y, OTA H, SATO T. Preparation of carbide fibres by thermal decomposition of cellulose-metal (Ti, Zr) alkoxide gel fibres., 1994, 13(7): 516–518.

[8] CUI X M, NAM Y S, LEE J Y,Fabrication of zirconium carbide (ZrC) ultra-thin fibers by electrospinning., 2008, 62(12/13): 1961–1964.

[9] NAM Y S, CUI X M, JEONG L,Fabrication and characterization of zirconium carbide (ZrC) nanofibers with thermal storage property., 2009, 517(24): 6531–6538.

[10] FIRBAS P, SEEBER A, CHENG Y B. Creation of titanium and zirconium carbide fibers with the forcespinning technique., 2016, 13(4): 619–628.

[11] SHE J, ZHAN Y, PANG M,synthesized (ZrB2+ZrC) hybrid short fibers reinforced Zr matrix composites for nuclear applications., 2011, 29(3): 401–404.

[12] LIU H Y, HOU X Q, WANG X Q,Fabrication of high-strength continuous zirconia fibers and their formation mechanism study., 2004, 87(12): 2237–2241.

[13] TAO X, QIU W, LI H,Synthesis of nanosized zirconium carbide from preceramic polymers by the facile one-pot reaction., 2010, 21(4): 300–304.

[14] DONG Z, ZHANG X, HUANG Q,Synthesis and pyrolysis behavior of a soluble polymer precursor for ultra-fine zirconium carbide powders., 2015, 41(6): 7359–7365.

[15] LI F, LIANG M, MA X F,Preparation and characterization of stoichiometric zirconium carbide foams by direct foaming of zirconia sols., 2015, 22(2): 493–500.

[16] WANG J X, NI D W, DONG S M,. Synthesis of nanocrystallized zirconium carbide based on an aqueous solution-derived precursor., 2017, 37(7): 22722–22727.

基于離心紡絲技術制備穩定的碳化鋯纖維

陳博文1,2,3, 王敬曉1,2, 姜佑霖1,2,3, 周海軍1,2, 廖春景1,2, 張翔宇1,2, 闞艷梅1,2, 倪德偉1,2

(1. 中國科學院 上海硅酸鹽研究所 高性能和超微結構國家重點實驗室, 上海 200050; 2. 中國科學院 上海硅酸鹽研究所 結構陶瓷與復合材料工程研究中心, 上海 200050; 3. 中國科學院大學, 北京 100049)

本研究提出了一種利用離心紡絲技術制備穩定碳化鋯(ZrC)纖維的有效方法。此方法使用醋酸鋯和蔗糖作為鋯源和碳源, 聚乙烯吡咯烷酮(PVP)作為紡絲助劑, 經過1600 ℃的裂解與碳熱還原熱處理后, 所紡原絲轉化成由均勻納米ZrC晶體組成的ZrC纖維。研究結果表明, 纖維中殘留的少量碳可助力ZrC纖維在2000 ℃的超高溫環境下仍保持較好的結構穩定性。

ZrC纖維; 離心紡絲; 超高溫穩定性

TQ174

A

2020-01-13;

2020-05-14

The National Key Research and Development Program of China (2016YFB0700202); National Natural Science Foundation of China (51702341); Chinese Academy of Sciences Innovative Funding (CXJJ-17-M169); The Key Deployment Project of Chinese Academy of Sciences (Y71YZ7171G); “CAS Pioneer Hundred Talents Program”

CHEN Bowen(1994–), male, PhD candidate. E-mail: chenbowen@student.sic.ac.cn

陳博文(1994–), 男, 博士研究生. E-mail: chenbowen@student.sic.ac.cn

NI Dewei, associate professor. E-mail: deweini@mail.sic.ac.cn

倪德偉, 副研究員. E-mail: deweini@mail.sic.ac.cn

1000-324X(2020)12-1385-06

10.15541/jim20200031